Lithium Australia Limited (ASX: LIT) has confirmed lithium ferro phosphate (LFP) cathode powder produced at its wholly owned subsidiary, VSPC Pty Ltd has been independently assessed at NOVONIX Battery Technology Solutions Inc.
NOVONIX is a manufacturer of some of the most accurate and precise lithium-ion battery cell testing equipment globally and a leading expert in battery materials research and development services.
This testing was undertaken as part of a customer joint materials selection program to independently validate the quality of VSPC LFP to support offtake development.
VSPC supplied a sample of its energy product for testing against two leading commercial brands.
The results demonstrated that VSPC’s LFP was the most stable of the three LFP samples tested and indicated that the combination of commercial grade graphite and VSPC’s LFP has the potential to support for long-lifetime cell designs. Such cells deliver sustained, continuous operation over a long period of time, often in aggressive conditions, making them ideal for use in applications ranging from EVs and grid energy storage, to e- scooters and e-bikes.
These results re-confirm Lithium Australia’s unwavering commitment to commercialising its LFP cathode manufacturing technology, providing customers with a solution to diversifying supply chain risks and a security of supply. North America, Europe and Australia remain key jurisdictions for potential commercial production, with pre-qualification in progress.
These independent results from NOVONIX confirm our belief that we have an LFP battery cathode material that currently competes with the best in the market. The results assist us in our current discussions with potential offtake partners and, consequently, takes us one step closer to bringing our pre-qualification plant to realisation,” Lithium Australia’s CEO, Simon Linge, said.
Lithium Ferro Phosphate
LFP is a type of lithium-ion battery chemistry that has gained significant popularity in recent years due to its excellent safety and long cycle life. LFP batteries are widely used in various applications, including EVs, grid energy storage systems, portable electronics, and backup power supplies.
One of the main advantages of LFP batteries is their high thermal stability, which makes them less prone to thermal runaway or fire compared to other lithium-ion chemistries. Additionally, LFP batteries offer a longer cycle life, meaning they can sustain a higher number of charge and discharge cycles without significant degradation.
Advances in LFP battery pack design have also significantly reduced the energy density gap with nickel/cobalt battery packs. These advantages have resulted in LFP batteries becoming increasingly popular for applications that require high performance, safety, and durability.
The increasing application of LFP was highlighted by Benchmark Mineral Intelligence in February 2023’s The Rise of LFP Batteries Outside of China (Benchmark Mineral Intelligence, 2023) which stated that:
also adopting the chemistry. Tata Motors in India is also using LFP.
Test Work Programme
Testing battery materials to get meaningful results for cell lifetimes and the rate of cell degradation can be a time-consuming process, involving charge/discharge cycling of test cells over thousands of cycles. However, this data is vital to assess the quality of a cathode like LFP that is valued for its long cycle life and slow rates of degradation.
VSPC cathode material has been tested by NOVONIX using their cell prototyping line and Ultra High Precision Coulometry (UHPC) equipment, which allows highly accurate measurements of the electrochemical processes in a cell in short periods of time.
This enables non-destructive testing of how battery chemistry is changing from cycle to cycle. UHPC allows for rapid selection of materials for favourable electrochemical properties, which correlate to long lifetime. In addition to UHPC testing, complementary cycle life testing is also underway. A VSPC (Energy) product and two commercial LFP products were tested with two different synthetic graphite counter electrodes, one from NOVONIX and a second from a leading tier 1 Chinese supplier. 1.0Ah stacked pouch cells were made from the six combinations of materials and a common benchmark electrolyte system. UHPC testing was performed at a slow current rate of C/10 for both charge and discharge (10 hour charge/discharge) at 40°C for 24 cycles. Cycle aging was performed at a C/3 charge and discharge (three hour charge/discharge) at 22°C and 40°C.
Test Results
Independent testing concluded that all LFP-Graphite combinations tested show good capacity retention in UHPC and long-term cycling at 22°C and 40°C. Therefore, this material combination is a good choice for a long lifetime battery design and application.
Initial results of this study support the high stability of VSPC LFP demonstrated by UHPC and cycle aging. Cells with VSPC LFP showed the lowest rate of capacity fade during UHPC testing and the highest electrochemical stability of the three LFP materials tested.
Cells with VSPC LFP and NOVONIX graphite demonstrated the strongest performance of all material combinations. VSPC LFP performed similarly to the other two commercial cathodes during cycle aging testing up to 400 cycles out of the planned 1,000 cycles.
Cells with VSPC LFP and NOVONIX graphite have retained about 97% of their initial capacity after 400 cycles at 22°C, compared to 93.5% for VSPC LFP with Graphite #2. Cycling is on-going to provide enough data to differentiate fully between the capability of the cathodes tested.